| S.No.
|
Test Description
|
I.S.- 4457:2007
|
IS - 15622:2017 Group B1b
|
Johnson Endura Tactile
|
Test Method
|
|
1.2 cm
|
1.5 cm
|
2.5 cm
|
|
A) Dimension Quality
|
|
Rectified
|
|
|
|
|
|
1
|
Deviation in Length & Width
|
±0.5%
|
±0.1%
|
±0.1%
|
±0.1%
|
±0.1%
|
IS 4457:2007 Annex B / ISO 10545-2
|
|
2
|
Deviation in Thickness
|
±5%
|
±5%
|
±4%
|
±4%
|
±4%
|
|
3
|
Straightness of Sides
|
±0.2%
|
±0.1%
|
±0.1%
|
±0.1%
|
±0.1%
|
|
4
|
Rectangularity
|
±0.2%
|
±0.1%
|
±0.1%
|
±0.1%
|
±0.1%
|
|
5
|
Surface Flatness
|
±0.3%
|
±0.5%
|
±0.3%
|
±0.3%
|
±0.3%
|
|
6
|
Surface Quality
|
Min 95%
|
Min 95%
|
Min 95%
|
Min 95%
|
Min 95%
|
|
B) Physical Properties
|
|
|
|
|
|
|
|
1
|
Water Absorption
|
< 0.5%
|
0.08<E<3
|
< 0.5%
|
< 0.5%
|
< 0.5%
|
IS 4457:2007 Annex C / ISO 10545-3
|
|
2
|
a) Scratch hardness of surface (Moh's scale) -Unglazed tile
|
_
|
>5
|
>7
|
>7
|
>7
|
IS 13630 part 13
|
|
b) Scratch hardness of surface (Moh's scale) -Glazed tile
|
_
|
>5
|
>6
|
>6
|
>6
|
|
3
|
Flexural Strength (Average MOR)
|
>35N/mm²
|
>30N/mm²
|
>38N/mm²
|
>38N/mm²
|
>38N/mm²
|
IS 4457:2007 Annex D / ISO 10545-4/IS 13630-6
|
|
4
|
Breaking Strength
|
>1300N
|
>1100N
|
>1600 N
|
>3000 N
|
>8500 N
|
IS 4457:2007 Annex D / ISO 10545-4/IS 13630-6
|
|
5
|
Impact Resistance
|
Manufacturer to declare
|
>0.55
|
>0.55
|
>0.55
|
>0.55
|
ISO 10545-5 /
IS 13630 -14
|
|
6
|
Deep Abrasion Resistance (Unglazed tile)
|
<175mm3
|
<175mm3
|
<120 mm3
|
<120 mm3
|
<120 mm3
|
IS 4457:2007 Annex E / ISO 10545- 6/IS 13630-12
|
|
7
|
Resistance to Surface Abrasion of Glazed Tiles for Floor Application
|
_
|
Class II, Min
|
Min PEI IV
|
Min PEI IV - V
|
Min PEI IV - V
|
ISO 10545-7 /IS 13630-11
|
|
8
|
# Skid Resistance
|
|
|
|
|
|
|
|
a) Skid Resistance - Ramp Test
|
Manufacturer to declare
|
Manufacturer to declare
|
>R9
|
>R9
|
>R9
|
DIN 51130
|
|
b) Coefficient of Friction
|
Manufacturer to declare
|
Manufacturer to declare
|
>0.42
|
>0.42
|
>0.42
|
ISO 10545 -17 /
ANSI A 326.3
|
|
9
|
Frost Resistance
|
_
|
_
|
No damage
|
No damage
|
No damage
|
ISO 10545-12 /
IS 13630-10
|
|
10
|
Density (gm/cc)
|
_
|
>2.0
|
>2.2
|
>2.2
|
>2.2
|
IS 13630 part 2
|
|
11
|
Moisture Expansion
|
Manufacturer to declare
|
Manufacturer to declare
|
<0.3mm/m
|
<0.3mm/m
|
<0.3mm/m
|
IS 13630-part 3 / ISO 10545-10
|
|
12
|
Color Resistance to UV Light
|
Report result
|
_
|
|
No change in color
|
No change in color
|
DIN 51094
|
|
C) Chemical Properties
|
|
|
|
|
|
|
|
1
|
Resistance to Concentrated HNO3 & H2SO4 Acid (wt. Loss)
|
<1.5 %
|
_
|
<0.8%
|
<0.8%
|
<0.8 %
|
IS 4457:2007 Annex G
|
|
2
|
Resistance to Chemicals
|
|
|
|
|
|
|
|
a) Resistance to Low concentrations of acids &
alkalies
|
Manufacturer to declare
|
Manufacturer to declare
|
ULA /GLA
|
ULA /GLA
|
ULA /GLA
|
ISO 10545-13
|
|
b) Resistance to High concentrations of acids &
alkalies
|
Manufacturer to declare
|
Manufacturer to declare
|
UHA /GHA
|
UHA /GHA
|
UHA /GHA
|
|
c) Resistance to household chemicals and swimming pool salts
|
Manufacturer to declare
|
UB /GB
|
UA /GA
|
UA /GA
|
UA /GA
|
|
3
|
Stain resistance
|
Resistant
|
Resistant
|
Resistant
|
Resistant
|
Resistant
|
IS 13630 part 7 /
ISO 10545-14
|
|
D) Thermal Properties
|
|
|
|
|
|
|
|
1
|
Linear Thermal Expansion
|
_
|
<7x10-6K-1
|
<7x10-6K-1
|
<7x10-6K-1
|
<7x10-6K-1
|
IS 13630 part 4 /
ISO 10545-8
|
|
2
|
Thermal shock resistance
|
No damage
|
No damage
|
No damage
|
No damage
|
No damage
|
IS 13630 part 5 /
ISO 10545-9
|
|
E) The profile of raised Button / Liner
|
|
|
|
|
|
|
|
20
|
Raised Button / Liner Height
|
_
|
_
|
4.5mm to 5.0mm
|
4.5mm to 5.0mm
|
|
DETR Standard Chapter 6 / ISO 23599:2012
|